ABSTRACT
Objective:To investigate the surface characterization,cell adhension and proliferation of ultrafine grained titanium (UFG Ti) after different sand blasting and acid-etching(SLA).Methods:The billets of UFG Ti and commercially pure titanium Ti(CP Ti) were incised into cylindrical specimens with 7 mm in diameter and 2 mm in height.The specimens were sand blasted at the air pressure of 0.2,0.4,0.6 and 0.8 MPa respectively(n =10) and then acid-etched.The surface morphology,roughness and surface wettability of the specimens were examined.Rat embryo osteoblasts MC3T3-E1 were cultured on the speciments for 1 d,3 d and 5 d respectively,the cell morphology and cell density were observed.Results:The different hierarchical porous topographies were formed on the surface of UFG and CP Ti after modified by SLA.The sizes of blasted holes on the surface and the surface roughness of both materials increased with the increase of blast pressure,but the values of UFG Ti were lower than those of CP Ti correspondingly(P ＜ 0.05).The surface wettability of them was also changed with the blast pressure,but the values of UFG Ti was significantly smaller than those of CP Ti(P ＜ 0.05).When the blast pressure was 0.6 Mpa,the UFG Ti exhibited excellent wettability,the cell density was the highest,the morphology of MC3T3-E1 cells on UFG Ti was superior to that on CP Ti.Conclusion:UFG Ti exhibits proper surface morphology,roughness and excellent wettability,which is more appropriate for adhension and proliferation of MC3T3-E1 cells after modification by SLA at blast pressure of 0.6 Mpa.